Details
Araldite 2015 is a two-component, sag resistant, semi-clear, room temperature curing gel epoxy adhesive with high shear and peel strength. The high-strength material is extremely tough and thixotropic (It’s a thick gel that can fill cracks and crevices). It is well suited for bonding SMC and GRP bonding, as well as bonding other dissimilar substrates including wood, concrete, rubber, glass, ceramics and other shop materials. Araldite 2015 A/B has a working time of approximately 30 minutes and handling strength in 4 hours. The adhesive gel is resistant to weathering and has a maximum service temperature of 100° C.
Additional Information
| SKU | HT4114608 |
|---|---|
| Former SKU | CR2015 ML50-K |
| Part Number | HT ARALDITE 2015-1 C US 50ML |
| Product Information | Huntsman Araldite 2015 is a sag-resistant, two- component, semi-clear, room temperature curing epoxy paste adhesive with high peel and shear strength. This toughened adhesive has high strength and is thixotropic. It is suitable for SMC and GRP bonding. Typical Use:
Araldite 2015 is a two component, room temperature curing, epoxy paste adhesive well suited for SMC and GRP bonding.
Appearance Mixed:
Neutral Paste
Density:
1.4
Viscosity at 25 Deg C:
Thixotropic
Pot Life at 25 Deg C, 100g:
30-40 Min
Gap Filling, Non-Sagging:
Up to 0.394 (10 mm) thickness
Mix Ratio:
100:100 Parts by weight and by volume
Cure time to reach LSS>145 psi:
12 hours @ 50 °F, 1 Hour @ 104 °F, 6 Minutes @ 212 °F
Cure time to reach LSS>1450 psi:
21 hours @ 50 °F, 2 Hours @ 104 °F, 7 Minutes @ 212 °F
Shelf Life:
3 years when stored properly
|
| Application | Two Part |
| Chemistry | Epoxy |
| Packaging | Cartridge |
| Product Category | Adhesives |
| Brand | HUNTSMAN |
| Industry | General Industrial |
| Manufacturer SKU | 4114608 |